Low alloy tool steel plate, AISI W2
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-10-30 23:01
- Browse the number:
139
Company Profile
- Dongguan Juli FRP Products Co., Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
No. 2 Dongyaun 1st Road, Lianhu 2th Industrial Zone, Tangxia Town, Dongguan, Guangdong, China (523712)
- Website: http://bozhong.brightonguitartuiton.com/
Product details
Model Number: ZXL141
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
Description:Low alloyed water-hardening tool steelApplications:Cold working tools for steels and metals when hard surface and tough core are demanded-tap drills, dies, broaching tools, stone working toolsChemical composition (in weight %)C 1.02
Si 0.20
Mn 0.23
V 0.10
Physical properties (average values) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 45.0
Electric resistivity [Ohm mm2/m]: 0.20
Specific heat capacity [J/g. K]: 0.46
Soft annealing:
Heat to 680 to 720°C, cool slowlyin furnace
This will produce maximum Brinell hardness of 213
Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to approx 600 to 650°C, holding for 1-2 hoursat heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening:
Harden from a temperature of 760 to 800°C followed bywater quenching
Hardness after quenching is about 65HRC
Forging:
Hot forming temperature: 1000 to 800°C
Specifications:
Grade: AISI W2
Standard: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery:
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Si 0.20
Mn 0.23
V 0.10
Physical properties (average values) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 45.0
Electric resistivity [Ohm mm2/m]: 0.20
Specific heat capacity [J/g. K]: 0.46
Soft annealing:
Heat to 680 to 720°C, cool slowlyin furnace
This will produce maximum Brinell hardness of 213
Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to approx 600 to 650°C, holding for 1-2 hoursat heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening:
Harden from a temperature of 760 to 800°C followed bywater quenching
Hardness after quenching is about 65HRC
Forging:
Hot forming temperature: 1000 to 800°C
Specifications:
Grade: AISI W2
Standard: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery:
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Han EV
price: Negotiable
-
Under Counter Beer Dispenser Cooler
price: Negotiable
-
Custom Latex Dog Toy
price: Negotiable
-
Empty Glass Cartridge Vial for Insulin Injector Pen
price: Negotiable
-
TM939 3-Ton Wheel Loader: Power and Versatility at Your Service
price: Negotiable
-
Frame Half Ram Electric Tricycle
price: Negotiable